The standard ASTM C a “Change in Height at Early Ages of Cylindrical Specimens from Cementitious Mixtures”  describes a method. ASTM C Standard Test Method for Change in Height at Early Ages of Cylindrical Specimens from Cementitious Mixtures. Lab ID: Use This test is used. ASTM A/AM Steel, Sheet and Strip, Heavy-Thickness Coils, Hot- Rolled, Carbon, Commercial, Drawing, Structural, High-Strength Low-Alloy.
|Published (Last):||23 February 2018|
|PDF File Size:||7.82 Mb|
|ePub File Size:||3.56 Mb|
|Price:||Free* [*Free Regsitration Required]|
Time for Results Please contact a CTLGroup chemical services representative or Project Manager to discuss your individual project needs and testing response times. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.
Results Produced All height change measurements will be reported as percent change over time. It is the responsibility of the user of this standard asttm establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Combining values asm the two systems may result in non-conformance with the standard. Print and complete the following order form. Instructions Submit all necessary materials to perform test including mixing instructions, mix design.
Further, the degree of restraint asrm which the specimen is subjected varies with the viscosity and degree of hardening of the mixture. MSDS must accompany all samples submitted.
These notes and footnotes shall not be considered as requirements of the test xstm. It is particularly applicable to grouting, patching, and form-filling operations where the objective is to completely fill a cavity or other defined space with a freshly mixed cementitious mixture that will continue to fill the same space at time of hardening.
ASTM C Height Change at Early Ages of Cementitious Mixtures | CTL
If you need more info or have any questions, please note the Lab ID number and contact us at: These include shrinkage or expansion asrm to hydration, settlement, evaporation, and other physical and chemical effects. Use This test is used to determine the change in height of a 3×6-in cylinder from the time of casting until final set is reached.
Historical C82 s – view previous versions of standard. If you need more info or have any questions, please note the Lab ID number and contact us at:.
Order Form 2 Email complete form to contact listed below. Contact Mike Morrison for additional information.
ASTM C827/C827M – 16
The maximum change in height will be reported, maximum decrease, maximum increase, change in height at set time and change in height at conclusion of test. However, the specimen used in this test method is not completely unrestrained so that the measurements are primarily useful for comparative purposes rather than as absolute values.
Link to Active This link will always route to the current Active version of the standard. It would be appropriate to use this test method as a basis for prescribing mixtures having restricted or specified volume change before the mixture becomes hard.